Thermal decomposition characteristics of microwave liquefied rape straw residues using thermogravimetric analysis

Document Type

Article

Publication Date

2-1-2018

Abstract

The thermal decomposition characteristics of microwave liquefied rape straw residues with respect to liquefaction condition and pyrolysis conversion were investigated using a thermogravimetric (TG) analyzer at the heating rates of 5, 20, 50 °C min−1. The hemicellulose decomposition peak was absent at the derivative thermogravimetric analysis (DTG) curve of liquefied residues, because it had been decomposed during the liquefaction. Furthermore, among the liquefied residues, the one from the reaction condition of 180 °C/15 min had the highest thermal stability under a high temperature (>700 °C). The DTG profiles revealed that raising the temperature heating rate could result in an increase in the maximum decomposition temperature. The apparent activation energy (Eα) values of the liquefied residues were lower than that of non-liquefied raw rape straw, whereas the recondensation reaction occurred at 180 °C/15 min remarkably increased the Eα. A noticeable increase in the Eα was observed for the liquefied residue from the 180 °C/10 min samples as the pyrolysis conversion increased from 0.15 to 0.55, suggesting a complex decomposition process with the increasing pyrolysis temperature. The liquefaction process could decrease the thermal decomposition temperature of biomass, which means higher reactivity and lower operational costs during pyrolysis.

Publication Source (Journal or Book title)

Journal of Thermal Analysis and Calorimetry

First Page

1911

Last Page

1918

This document is currently not available here.

Share

COinS